The effects of re-irradiation on the chemical and morphological properties of permanent teeth.

This study aimed to assess the in vitro effects of re-irradiation on enamel and dentin properties, simulating head and neck cancer radiotherapy retreatment. Forty-five human permanent molars were classified into five groups: non-irradiated; irradiated 60 Gy, and re-irradiated with doses of 30, 40, and 50 Gy. Raman spectroscopy, scanning electron microscopy (SEM), and energy dispersive x-ray spectroscopy (EDS) were employed for analysis. Raman spectroscopy assessed intensity, spectral area, and specific peaks comparatively. Statistical analysis involved Kolmogorov-Smirnov and One-Way ANOVA tests, with Tukey's post-test (significance level set at 5%). Significant changes in irradiated, non-irradiated, and re-irradiated enamel peaks were observed, including phosphate (438 nm), hydroxyapatite (582 nm), phosphate (960 nm), and carbonate (1070 nm) (p < 0.05). Re-irradiation affected the entire tooth (p > 0.05), leading to interprismatic region degradation, enamel prism destruction, and hydroxyapatite crystal damage. Dentin exhibited tubule obliteration, crack formation, and progressive collagen fiber fragmentation. EDX revealed increased oxygen percentage and decreased phosphorus and calcium post-reirradiation. It is concluded that chemical and morphological changes in irradiated permanent teeth were dose-dependent, exacerbated by re-irradiation, causing substantial damage in enamel and dentin.

Influence of preventive remineralizing techniques on surface roughness and volume loss of dentin submitted to erosive and/or abrasive challenges.

Background: The objective this study was to evaluate the influence of preventive remineralizing techniques on surface roughness and volume loss of dentin submitted to erosive and/or abrasive challenges. Material and Methods: One hundred and eighty specimens of bovine root dentin were made; half of each was isolated (without treatment - WT) and half was subjected to the following remineralizing techniques: fluoride varnish (FV); Regenerate Boosting Serum® (RBS); Er,Cr:YSGG laser (L); fluoride varnish+laser (FV+L); Regenerate Boosting Serum®+laser (RBS+L). The specimens were submitted to erosive, abrasive and erosive followed by abrasive challenge. Erosion was carried out for 5 minutes, twice a day for 10 days. Abrasion was performed with an electric toothbrush and slurry solution for 60 seconds. The evaluation was performed by confocal laser scanning microscopy. Analysis of variance and Tukey tests were used for surface roughness; volume loss comparison was performed using the Kruskal-Wallis test and Dunn's post-hoc (p<0.05). Results: There was no statistically significant difference in the surface roughness of the reference area in relation to the areas submitted to different types of treatment and challenges (p>0.05). Regarding volume loss, the untreated group submitted to erosive/abrasive challenges showed greater percentage of volume loss compared to the other groups (p<0.05). Conclusions: It is concluded that preventive remineralizing techniques are effective in maintaining dentin volume after erosive/abrasive challenges. Key words:YSGG lasers, Dentin, Erosion, Tooth Abrasion.

Efficacy of ClinproTMXT Varnish surrounding brackets on the enamel surface of white spot lesion.

Orthodontics patients usual develop demineralization and present cavity caries lesions after six months. Minimally invasive procedures have been the goal in modern dental practice. The aim of this study was to evaluate the effect of ClinproTMXT Varnish, on the enamel surface roughness and severity of white spot lesions. Twenty premolars were submitted to bond brackets and experimental induction of demineralization and randomly divided into 2 groups: GI - fluoride varnish (Colgate Duraphat®); GII - Ionomeric Sealant (ClinproTMXT Varnish). The treatment was applied around the brackets. The surface roughness of specimens was analyzed, before treatment and 12 weeks after treatment by laser confocal microscopy, and the severity of the white spot lesion was by laser fluorescence device. The data were analyzed by non-parametric Wilcoxon and Mann-Whitney Test, at 5% significance, roughness percentage reduction was performed. The severity of demineralization decreased in both, GI (p = 0.005) and GII (p = 0.019). Enamel superficial roughness levels decreased in GI and GII. As well as the roughness percentage, being more expressive in the ClinproTMXT Varnish group (85,09%). Colgate Duraphat® or Clinpro™ XT Varnish reduced the severity of the demineralization and decreased the superficial roughness on the enamel. The Clinpro™ XT Varnish was superior to superficial roughness on enamel.

Proteomic analysis of stimulated saliva in gastroesophageal reflux disease patients with and without erosive tooth wear: Observational study.

OBJECTIVE: To evaluate the difference in the proteomic profile of stimulated saliva in patients with gastroesophageal reflux disease (GERD) with (GE) and without (GNE) erosive tooth wear (ETW), regarding both human and bacterial proteins. METHODS: Stimulated saliva (SS) was collected from 16 patients (8/group). Samples were centrifuged at 4.500 g for 15 min under refrigeration to remove all debris. The supernatant from each saliva sample was taken and frozen at -80 °C. After extracting the proteins, they were submitted to reverse phase liquid chromatography and mass spectrometry (nLC-ESI-MS/MS). Label-free proteomic quantification was performed using Protein Lynx Global Service (PLGS) software (p < 0.05) for human and bacterial proteins. RESULTS: In total, 67 human proteins were common for GNE and GE groups. GNE group presented, compared to GE group, increase in proteins that confer antimicrobial and acid resistant properties, such as cystatins, histatin and immunoglobulins. However, GNE group had a marked decrease in subunits of hemoglobin (α, ß and delta). Regarding bacterial proteins, for SS, 7 and 10 unique proteins were identified in the GE and GNE groups, respectively. They are related to protein synthesis and energy metabolism and interact with human proteins typically found in saliva and supramolecular complexes of the acquired pellicle. CONCLUSIONS: Our data indicate that the stimulation of the salivary flow increases acid resistant and antimicrobial proteins in saliva, which might protect against ETW. CLINICAL SIGNIFICANCE: This pioneer study showed important differences in the human and bacterial proteome of SS in patients with GERD with or without ETW.

Acquired enamel pellicle protects gastroesophageal reflux disease patients against erosive tooth wear.

The objective of this study was to compare the protein profile of the acquired enamel pellicle (AEP) formed in vivo in patients with or without gastroesophageal reflux disease (GERD), and with or without erosive tooth wear (ETW). Twenty-four volunteers were divided into 3 groups: 1) GERD and ETW; 2) GERD without ETW; and 3) control (without GERD). The AEP formed 120 min after prophylaxis was collected from the lingual/palatal surfaces. The samples were subjected to mass spectrometry (nLC-ESI-MS/MS) and label-free quantification by Protein Lynx Global Service software. A total of 213 proteins were identified, or 119, 92 and 106 from each group, respectively. Group 2 showed a high number of phosphorylated and calcium-binding proteins. Twenty-three proteins were found in all the groups, including 14-3-3 protein zeta/delta and 1-phosphatidylinositol. Several intracellular proteins that join saliva after the exfoliation of oral mucosa cells might have the potential to bind hydroxyapatite, or participate in forming supramolecular aggregates that bind to precursor proteins in the AEP. Proteins might play a central role in protecting the dental surface against acid dissolution.

Efficacy of ClinproTMXT Varnish surrounding brackets on the enamel surface of white spot lesion

Abstract Orthodontics patients usual develop demineralization and present cavity caries lesions after six months. Minimally invasive procedures have been the goal in modern dental practice. The aim of this study was to evaluate the effect of ClinproTMXT Varnish, on the enamel surface roughness and severity of white spot lesions. Twenty premolars were submitted to bond brackets and experimental induction of demineralization and randomly divided into 2 groups: GI - fluoride varnish (Colgate Duraphat®); GII - Ionomeric Sealant (ClinproTMXT Varnish). The treatment was applied around the brackets. The surface roughness of specimens was analyzed, before treatment and 12 weeks after treatment by laser confocal microscopy, and the severity of the white spot lesion was by laser fluorescence device. The data were analyzed by non-parametric Wilcoxon and Mann-Whitney Test, at 5% significance, roughness percentage reduction was performed. The severity of demineralization decreased in both, GI (p = 0.005) and GII (p = 0.019). Enamel superficial roughness levels decreased in GI and GII. As well as the roughness percentage, being more expressive in the ClinproTMXT Varnish group (85,09%). Colgate Duraphat® or Clinpro™ XT Varnish reduced the severity of the demineralization and decreased the superficial roughness on the enamel. The Clinpro™ XT Varnish was superior to superficial roughness on enamel.

Resumo Pacientes ortodônticos geralmente desenvolvem desmineralização e apresentam lesões de cárie após seis meses de tratamento. Procedimentos minimamente invasivos têm sido o objetivo na prática odontológica moderna. O objetivo deste estudo foi avaliar o efeito do ClinproTM XT selante ionomérico, ao redor do bráquete, com relação a rugosidade superficial do esmalte e a severidade da lesão induzida. Vinte pré-molares foram submetidos a colagem de bráquetes e indução experimental de desmineralização e divididos aleatoriamente em 2 grupos: GI - verniz fluoretado (Colgate Duraphat®); GII - Selante Ionomérico (ClinproTM XT). O tratamento foi aplicado ao redor dos bráquetes. A rugosidade da superfície dos espécimes foi analisada, antes do tratamento e 12 semanas após o tratamento por microscopia confocal a laser e severidade da lesão de mancha branca por dispositivo de fluorescência a laser. Os dados foram analisados pelo teste não paramétrico de Wilcoxon e Mann-Whitney, a 5% de significância. A taxa de redução da lesão foi calculada. A severidade da desmineralização diminuiu tanto no GI (p = 0,005) quanto no GII (p = 0,019). Os níveis de rugosidade superficial do esmalte diminuíram no GI e GII, assim como o percentual de rugosidade, sendo mais expressivo no grupo ClinproTMXT (85,09%). Colgate Duraphat® e Clinpro™ XT reduziram a severidade da desmineralização e diminuíram a rugosidade superficial do esmalte. O selante ionomérico Clinpro™ XT foi superior na redução percentual de rugosidade.

Treatment outcome for dentin hypersensitivity with laser therapy: Systematic review and meta-analysis.

BACKGROUND: Laser protocols for the treatment of dentin hypersensitivity (DH) have not yet been studied systematically. OBJECTIVES: The present study aimed to review clinical trials on the treatment of DH with laser therapy through a systematic review and meta-analysis. MATERIAL AND METHODS: The search of electronic databases resulted in 562 publications up to April 2020. The inclusion criteria were studies carried out on humans and reporting on the treatment of DH with laser therapy. Case reports, literature reviews and systematic reviews were excluded. Selected by abstract, potentially eligible papers were read in full (n = 160). Independent examiners performed data extraction and the assessment of the risk of bias. RESULTS: A total of 34 studies were included in the analysis, and 11 in the quantitative analysis. It was observed that most studies followed up patients for a maximum of 6 months (55%). Through the meta-analysis, we observed statistically significant differences between the average pain before and after 3 months of treatment with highand low-power lasers. However, through indirect comparisons, it was observed that the high-power laser showed a greater tendency to reduce the pain levels after 3 months of treatment as compared to the low-power laser, but without a statistically significant difference. CONCLUSIONS: It was possible to conclude that regardless of the type of laser used in the treatment of DH, this treatment is an effective option for the control of pain symptoms. However, it was not possible to establish a defined treatment protocol, since the evaluation methods are very different from each other. Text for Rewiew and clinical cases.

In vitro study of structural and mechanical properties of latex and non-latex intermaxillary orthodontic elastics.

PURPOSE: We evaluated bacterial endotoxin adhesion, superficial micromorphology and mechanical properties of latex and non-latex intermaxillary orthodontic elastics. METHODS: To quantify the adhered bacterial endotoxin, elastics were divided into 5 groups: experimental (n = 12) latex and non-latex elastics, previously contaminated by an endotoxin solution, negative control (n = 6) latex and non-latex elastics without contamination, and positive control (n = 6) stainless steel specimens (metallic replicas), contaminated by an endotoxin solution. In parallel, the structural micromorphology (n = 6) and surface roughness of latex and non-latex intermaxillary orthodontic elastics were assessed using confocal laser microscopy. Force degradation (g) and deformation of the internal diameter change (mm) were also evaluated. Structural micromorphology, surface roughness (µm), force degradation (g) and internal diameter (mm) change were evaluated at time 0 and after 24 and 72 h in a deformation test. Data were analyzed by the Shapiro-Wilk, Kruskal-Wallis, Dunn, ANOVA and Bonferroni tests (α = 5%). RESULTS: Endotoxin adhered similarly to both types of elastics with scores of 3 (> 1.0 EU/mL). The surface microstructure of both types of elastics showed irregularities and porosities at all times. Initially, the latex elastics had a higher surface roughness (p < 0.001) than the non-latex ones. After 24 h loading, surface roughness of the latex elastics was significantly reduced (p < 0.001), while after 72 h, the values were similar for both types (p > 0.05). The non-latex elastics had significantly higher force generation values (p < 0.05) at 0, 24 and 72 h compared with the latex elastics, although there was a significant reduction (p < 0.001) in force over time for both elastics. Despite similar initial values, non-latex elastics had a significantly larger internal diameter (p < 0.001) after the loading periods of 24 and 72 h compared with the latex elastics. CONCLUSION: Both elastics showed high affinity with endotoxin and microstructural irregularities of their surface. The non-latex elastics generated higher force values but demonstrated greater deformation of the internal diameter after loading.

Acquired enamel pellicle protects gastroesophageal reflux disease patients against erosive tooth wear

Abstract The objective of this study was to compare the protein profile of the acquired enamel pellicle (AEP) formed in vivo in patients with or without gastroesophageal reflux disease (GERD), and with or without erosive tooth wear (ETW). Twenty-four volunteers were divided into 3 groups: 1) GERD and ETW; 2) GERD without ETW; and 3) control (without GERD). The AEP formed 120 min after prophylaxis was collected from the lingual/palatal surfaces. The samples were subjected to mass spectrometry (nLC-ESI-MS/MS) and label-free quantification by Protein Lynx Global Service software. A total of 213 proteins were identified, or 119, 92 and 106 from each group, respectively. Group 2 showed a high number of phosphorylated and calcium-binding proteins. Twenty-three proteins were found in all the groups, including 14-3-3 protein zeta/delta and 1-phosphatidylinositol. Several intracellular proteins that join saliva after the exfoliation of oral mucosa cells might have the potential to bind hydroxyapatite, or participate in forming supramolecular aggregates that bind to precursor proteins in the AEP. Proteins might play a central role in protecting the dental surface against acid dissolution.

In vitro effect of two resin based materials for treating initial caries lesion around braces, under cariogenic challenge.

Background: Orthodontic treatment makes the patient susceptible to the development of white spot lesions (WSL) due to the greater accumulation of bacterial plaque. The purpose of this in-vitro study was to evaluate the preventive effect of two resin materials on the incidence of these lesions in the region adjacent to the fixed bracket bonded under a WSL-treated area by two resin materials. Material and Methods: 36 extracted human molars presenting natural WSL were included. They were randomly divided into 2 groups for intervention: IC (Infiltration resin Icon®) and PS (resin sealant Pro Seal ®). Braces were bonded just above the WSL. The enamel surface around the brace was treated by one of the tested materials, leaving another part to be control. The samples were submitted again to a cariogenic challenge. The exposed enamel non-treated area from booth groups comprised the control group (E). For morphological analysis, confocal images were taken at baseline, after treatment, and after pH cycling of each sample. Lesion depth were measured (µm) and compared to the enamel thickness to calculate a demineralization index. All groups were compared using the Kruskal Wallis test and Dunn's post-test. Results: PS group showed the lowest demineralization index (0.27 µm) when compared to the control area (0.39 µm) (p<0.05). IC presented a slightly higher percentage of lesions when compared to PS, however, did not differ significantly from the control exposed area. Conclusions: The resin sealant Pro Seal® had a positive protective effect under white spot environmental area and Icon® infiltrant, although showed some protection, did not statistically differ from controls. Key words:Dental Caries, Orthodontics, Dental Enamel, Sealants.

Effect of an experimental chitosan/casein gel on demineralized enamel under a cariogenic challenge.

BACKGROUND: Dental caries is considered one of the most common oral health diseases. OBJECTIVES: The aim of the study was to evaluate the effects of an experimental chitosan/casein gel on enamel demineralization/remineralization in an environment with a high cariogenic challenge. MATERIAL AND METHODS: Thirty-six specimens of bovine enamel (4 mm × 3 mm × 2 mm) were ground flat and polished. Then, the specimens were immersed in acetate buffer for 43 h with half of the surface protected (serving as control) and the other half exposed. All demineralized surfaces were randomly assigned into 3 groups (n = 12 per group) according to the type of treatment (G1 - control, G2 - 1.5% chitosan gel with 1.5% casein, and G3 - 1.5% chitosan gel without casein), and the corresponding treatment was applied once a week for 3 weeks. The specimens were also subjected to pH cycles of demineralization/ remineralization and the treatments were performed 3 times at 7-day intervals for a total of 21 days. Surface images were obtained for the analysis of initial roughness and, after the cariogenic challenge, new images were obtained to evaluate the final roughness, volume loss and wear profile using laser confocal microscopy. After the analyses, the specimens were cut and the depth of demineralization was measured. The data were analyzed using the Kruskal-Wallis analysis of variance (ANOVA) and the Tukey's test. RESULTS: While the chitosan gel with casein showed a similar loss to the control group (p > 0.05), both gels resulted in similar volume loss (p > 0.05). There were no statistical differences regarding the wear profile, surface roughness and depth of demineralization between the groups (p > 0.05). CONCLUSIONS: The chitosan gel reduced volume loss of the demineralized enamel without significantly impacting the surface smoothness.

Enhanced mechanical properties, anti-biofilm activity, and cytocompatibility of a methacrylate-based polymer loaded with native multiwalled carbon nanotubes.

OBJECTIVES: We aimed to optimize the mechanical and biological properties of a conventional methacrylate-based dental polymer by loading it with double- and triple-walled carbon nanotubes as growth (DTWCNTG). METHODS: A formulation of bisphenol A-glycidyl methacrylate and triethylene glycol dimethacrylate (mass ratio = 2:1) was mixed with DTWCNTG at concentrations of 0.0% (control), 0.001%, 0.005%, and 0.010%. The concentrations were physicochemical and morphologically evaluated, and antibacterial activity was assessed by seeding a Streptococcus mutans strain (ATCC 25175) on the experimental polymeric surfaces. Cellular survival and osteodifferentiation were evaluated in epithelial (HaCat) and preosteoblast cells (MC3T3-E1). RESULTS: The 0.001% DTWCNTG concentration yielded higher compressive strength, elastic modulus, flexural strength, flexural modulus, water sorption, and solubility than the control. The degree of conversion and color did not significantly change with a low amount of DTWCNTG incorporated into the polymer. Antibacterial activity significantly improved when tested on the 0.001% DTWCNTG discs. No groups showed cytotoxicity in a short-term analysis and adding DTWCNTG favored MC3T3-E1 mineralization over the control, particularly in the 0.001% formulation. SIGNIFICANCE: The micro-addition of 0.001% DTWCNTG confers mechanical resistance, antimicrobial properties, and bioactivity to methacrylate-based polymers without significantly compromising color. Incorporating DTWCNTG improved dental composite properties and could be a biomodified material for minimally invasive procedures.

Photoelastic, microhardness and roughness analysis of zirconia and stainless steel crowns for primary molars.

PURPOSE: To compare the stress distribution through photoelasticity, microhardness and roughness of intact crowns of primary molars (CC) and the preformed crowns of stainless steel (SSC) and zirconia (ZC) used in dental restorations in pediatric dentistry. METHODS: Six healthy primary molars were selected. For the photoelastic models, the teeth were fixed in photoelastic resin. A load of 100 N was applied, and the models were analyzed by transmission polariscope. The Tardy method was used to quantify the fringe order which calculates the maximum stress (T) value in each selected point. The teeth were prepared for cementation of the crowns. The photoelastic test was repeated for each experimental crown. Knoop microhardness was assessed on the buccal surfaces of the CCs, SSCs, and ZCs using a microhardness tester. Parameters were 50 gf for 5 seconds. Roughness was evaluated using a confocal 3-D laser scanning microscope/software at 216x magnification. Roughness average (Ra) values from each model (expressed in µm) were collected and group means were calculated. The stress distribution, microhardness, and roughness data were compared by using one-way ANOVA and the Tukey's test (α= 0.05). RESULTS: There was no difference in the stress distribution for the CCs, SSCs and ZCs. For the microhardness analysis, the ZCs obtained the highest values compared to the CCs and the SSCs (P< 0.001). The CCs were significantly higher than the SSCs (P= 0.027). There was no difference in roughness for the three models (P= 0.615). The SSCs and ZCs showed satisfactory mechanical behavior. CLINICAL SIGNIFICANCE: The use of preformed crowns, especially those made of esthetic materials, is currently increasing in the field of pediatric dentistry. The knowledge of mechanical properties of stainless steel- and zirconia-prefabricated crowns provides scientific foundation for safe clinical application, especially in primary teeth.

Influence of diode laser treatment and casein phosphopeptide-amorphous calcium phosphate paste on eroded root dentin.

Introduction: It is still unclear whether the pretreatment for dentin hypersensitivity can interfere with the adhesive-dentin bonding strength. This study aimed to evaluate in vitro the effect of pretreatment with a casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) paste and diode laser on the shear bond strength of the etch-and-rinse adhesive system in the adhesive-dentin interface. Materials and Methods: Seventy-five bovine root specimens were randomly divided into five experimental groups (n = 15). Samples were eroded by six cycles of immersion in hydrochloric acid solution (0.01M; pH = 1.2) for 20 s each, at 45 min intervals, and treated with: G2 - no treatment, G3 - CPP-ACP, G4 - diode laser (970 nm), and G5 - CPP-ACP + Diode laser. After treatments, the morphology of the specimens was analyzed. Results: The fracture mode of each group was evaluated after restoration with composite resins in the treated area. Data were analyzed by the one-way ANOVA and Tukey's test (P < 0.05). G3 showed the highest values for shear bond strength; there was no significant difference among G1, G3, and G5 (P > 0.05). The adhesive fracture was predominant for all groups. Conclusion: The use of desensitizers containing CPP-ACP, associated or not with a diode laser, increased the bond strength of the etch-and-rinse adhesive system on eroded root dentin.

Impact of Endodontic Kinematics on Stress Distribution During Root Canal Treatment: Analysis of Photoelastic Stress.

INTRODUCTION: Structural defects created by endodontic treatment are the most common cause of major dental failures. This study analyzed levels of stress produced by endodontic instruments during the root canal treatment by photoelastic analysis of stress. METHODS: Twenty-four human premolars were randomly divided into 4 groups (n = 6) according to instrumentation protocol: ProTaper Next (GPT), One Shape (GOS), Wave One Gold (GWO), and TF Adaptive (GTF). The evaluation of the photoelastic model was performed at 4 dental zones: dental-crown region, cervical third of root, middle third of root, and apical third of root. Silicone molds were prepared (2 × 15 mm), and pinjets were used inside the root canals to fixate teeth. Photoelastic resin (2:1 ratio) was poured into the silicone molds to form photoelastic models. A transmission polariscope was used to analyze the positions of interest and recorded with a digital camera. Tardy's method was used to quantify the fringe order (n) and calculate the maximum stress value (τ) at each selected point. Data were analyzed with two-way analysis of variance, Tukey test (P < .05), fringe descriptive analysis. RESULTS: All groups showed a significant increase in the level of stress created during biomechanical preparation of the root canals. In the quantitative analysis, there was no statistically significant difference among the groups (P > .05). In the qualitative analysis, GPT and GTF instruments achieved greater levels of stresses compared with GWO and GOS instruments. At the beginning of instrumentation, stresses were concentrated at the coronary level and the end of instrumentation at the middle and apical root level. CONCLUSIONS: All endodontic systems resulted in accumulation of stress along the dental structure. Stress was found in different concentrations along the tooth and at different levels.

Microhardness homogeneity of RBCs light-cured with a multiple-peak LED and surface characterization after wear.

This in vitro study evaluated the effect of the beam homogeneity of a multiple-peak light-curing unit on the surface microhardness and the effect of toothbrushing wear on the microhardness, surface roughness, roughness profile, volume loss, and gloss retention of incremental and bulk-fill resin-based composites (RBCs). A LED light-curing unit (VALO) with four LEDs at the tip end (405, 445, 465A, and 465B nm emission peak) was used according to each manufacturer-recommended time to obtain disks (n=10) of six RBCs: Estelite Sigma Quick, Charisma Classic, Tetric EvoCeram Bulk Fill, Filtek Z250, Filtek Supreme Ultra, and Filtek Bulk Fill. Microhardness values were obtained according to each LED positioning of the light-curing unit on the top surface of the RBCs and were analyzed before and after toothbrushing regarding microhardness, surface roughness, roughness profile, volume loss, and gloss retention. Microhardness was considered homogeneous on the top surface regardless of the type of RBC or wavelength tested (p>0.05). Overall, toothbrushing did not reduce the microhardness of the RBCs but influenced the gloss values for most RBCs (p<0.001). Charisma Classic presented the greatest surface roughness and roughness profile after toothbrushing (p<0.05). Volume loss did not differ among RBCs (p>0.05). In conclusion, different wavelengths of the LED did not affect the top surface microhardness, regardless of the RBCs tested; and bulk-fill composites presented similar surface changes (microhardness, surface roughness, roughness profile, volume loss, and gloss retention) when compared to conventional composites after toothbrushing.

Sports mouthguards: Contamination, roughness, and chlorhexidine for disinfection - A randomized clinical trial

Abstract The aim of the present in vivo study was to evaluate the bacterial contamination of sports mouthguards, surface roughness, and the efficacy of chlorhexidine gluconate spray in the disinfection of these devices. A randomized, blinded cross-over clinical trial was performed with twenty 9 to 13 years old children who practiced martial arts and participated in all phases of the study. They were instructed to wear mouthguards 3 alternated days a week for 1 hour and, after use, to spray sterile tap water or chlorhexidine 0.12%. The mouthguards were analyzed by MTT assay, Checkerboard DNA-DNA hybridization, and confocal laser microscopy prior and after use for 2 weeks. Data were analyzed by Wilcoxon and t-Student, and Pearson correlation tests, with 5% significance level. Were observed that mouthguards of the control group were more contaminated with cariogenic microorganisms than those of the chlorhexidine group (p<0.05). The mouthguards use of spray of chlorhexidine reduced significantly the bacteria contamination compared with control group (p = 0.007). The surface roughness of the mouthguards increased significantly after use, irrespective of application of chlorhexidine spray. A moderate correlation (r=0.59) was observed between surface roughness and the cariogenic microorganism's contamination only for control group. Sports mouthguards had intense microbial contamination and increased surface roughness after its use. The use of chlorhexidine spray was effective for reducing the mouthguards contamination used by children.

Resumo O objetivo do presente estudo in vivo foi avaliar a contaminação bacteriana de protetores bucais esportivos, a rugosidade da superfície e a eficácia do spray de gluconato de clorexidina na desinfecção desses dispositivos. Um ensaio clínico randomizado, cego, cruzado foi realizado com vinte crianças de 9 a 13 anos, que praticavam artes marciais, participaram de todas as fases do estudo. As crianças foram orientadas a usar o protetor bucal por 3 dias alternados durante 1 hora e, após o uso, borrifar água de torneira estéril ou clorexidina 0,12%. Os protetores foram analisados por ensaio MTT, Hibridização DNA-DNA e microscopia confocal a laser antes e após o uso por 2 semanas. Os dados foram analisados pelos teste de Wilcoxon, teste t de Student, e correlação de Pearson, com nível de significância de 5%. Observou-se que os protetores bucais do grupo controle estavam mais contaminados com microrganismos cariogênicos do que os do grupo experimental (clorexidina) (p <0,05). O uso de protetores bucais com spray de clorexidina reduziu significativamente a contaminação bacteriana em relação ao grupo controle (p = 0,007). A rugosidade da superfície dos protetores bucais aumentou significativamente após o uso, independentemente da aplicação de spray de clorexidina. Uma correlação moderada (r = 0,59) foi observada entre a rugosidade da superfície e a contaminação do micro-organismo apenas para o grupo controle. Os protetores bucais esportivos apresentam intensa contaminação microbiana e aumento da rugosidade superficial após o uso. O uso de spray de clorexidina foi eficaz para reduzir a contaminação dos protetores bucais usados por crianças.

Microhardness homogeneity of RBCs light-cured with a multiple-peak LED and surface characterization after wear

Abstract This in vitro study evaluated the effect of the beam homogeneity of a multiple-peak light-curing unit on the surface microhardness and the effect of toothbrushing wear on the microhardness, surface roughness, roughness profile, volume loss, and gloss retention of incremental and bulk-fill resin-based composites (RBCs). A LED light-curing unit (VALO) with four LEDs at the tip end (405, 445, 465A, and 465B nm emission peak) was used according to each manufacturer-recommended time to obtain disks (n=10) of six RBCs: Estelite Sigma Quick, Charisma Classic, Tetric EvoCeram Bulk Fill, Filtek Z250, Filtek Supreme Ultra, and Filtek Bulk Fill. Microhardness values were obtained according to each LED positioning of the light-curing unit on the top surface of the RBCs and were analyzed before and after toothbrushing regarding microhardness, surface roughness, roughness profile, volume loss, and gloss retention. Microhardness was considered homogeneous on the top surface regardless of the type of RBC or wavelength tested (p>0.05). Overall, toothbrushing did not reduce the microhardness of the RBCs but influenced the gloss values for most RBCs (p<0.001). Charisma Classic presented the greatest surface roughness and roughness profile after toothbrushing (p<0.05). Volume loss did not differ among RBCs (p>0.05). In conclusion, different wavelengths of the LED did not affect the top surface microhardness, regardless of the RBCs tested; and bulk-fill composites presented similar surface changes (microhardness, surface roughness, roughness profile, volume loss, and gloss retention) when compared to conventional composites after toothbrushing.

Resumo Este estudo in vitro avaliou a homogeneidade do feixe de um fotopolimerizador de múltiplos picos na microdureza superficial e o efeito da escovação na microdureza, rugosidade superficial, perfil de rugosidade, perda de volume e retenção do brilho de compósitos a base de resina (RBCs) incrementais ou bulk-fill. Um fotopolimerizador LED (VALO) com quatro LEDs na ponteira (405, 445, 465A e 465B nm de pico de emissão) foi usado de acordo com o tempo recomendado por cada fabricante para obtenção de discos (n=10) de seis RBCs: Estelite Sigma Quick, Charisma Classic, Tetric EvoCeram Bulk Fill, Filtek Z250, Filtek Supreme Ultra e Filtek Bulk Fill. Os valores de microdureza foram obtidos seguindo o posicionamento de cada LED na superfície superior das amostras e foram analisados antes e após a escovação quanto a microdureza, rugosidade superficial, perfil de rugosidade, perda de volume e retenção do brilho. A microdureza foi considerada homogênea no topo da superfície, independentemente do tipo de RBCs ou comprimento de onda testados (p>0.05). No geral, a escovação não reduziu a microdureza das RBCs, mas influenciou o brilho para a maioria das RBCs (p<0.001). Charisma Classic apresentou os maiores valores de rugosidade superficial e perfil de rugosidade após a escovação (p<0.05). A perda de volume não diferiu entre as RBCs (p>0.05). Em conclusão, os diferentes comprimentos de onda do LED não alteraram a microdureza do topo da superfície, independentemente das RBCs testadas; e as resinas bulk-fill apresentaram alterações superficiais similares (microdureza, rugosidade superficial, perfil de rugosidade, perda de volume e manutenção do brilho) quando comparadas às resinas convencionais após a escovação.

Color Stability and Surface Roughness of Hybrid and Nanofilled Composites Brushed with Abrasive Dentifrices / Estabilidade de Cor e Rugosidade Superficial de Resinas Compostas Micro-Híbridas e Nanoparticulada Submetidas à Escovação com Dentifrícios Abrasivos

The aim of this study was to evaluate the color stability and the surface roughness of different composites brushed with toothpastes presenting different levels of abrasivity. Thirty discs of each material were obtained using michohybrid composites (Brilliant NG and Charisma Diamond) and a nanocomposite (Filtek Z350XT). The initial color (CIELab) and surface roughness (confocal laser scanning microscopy) of resin discs were evaluated. Afterwards, 10 specimens per group were brushed with the following dentifrices: Maximum Cavity Protection, Sensodyne Repair & Protect and Colgate Sensitive Pro-Relief. Brushing was performed with an electric toothbrush equipped with soft bristle head, with standard power and weight, for 30 minutes. Every 30 seconds, 1.0 ml of the slurry was injected between the bristles of the brush and the specimen. After abrasive challenge, the samples had their color and roughness reevaluated. Data were submitted to the Kruskal-Wallis test (color change) or the t-test (surface roughness). The level of significance was 5%. Results: Brushing did not significantly change the color of the composites tested in the study herein . On the other hand, the surface roughness of the composites was significantly affected by the abrasive challenge, regardless of the toothpaste used. The surface roughness change was similar for all the composites. The abrasive challenge with the toothpastes Maximum Cavity protection, Sensodyne Repair & Protect and Colgate Sensitive Pro-Relief was not able to significantly change the color of the composite resins. Nevertheless, the abrasive challenges significantly altered the surface roughness of all the evaluated composites. However, the changes in surface roughness were statistically similar in the microhybrid and nanofilled composites. (AU)

O objetivo deste estudo foi avaliar a estabilidade de cor e a rugosidade superficial de diferentes resinas compostas escovadas com dentifrícios de diferentes níveis de abrasividade. Trinta discos de cada material foram obtidos utilizando compósitos micro-híbridos (Brilliant NG e Charisma Diamond) e um nanocompósito (Filtek Z350XT). A cor inicial (CIELab) e a rugosidade superficial (microscopia confocal de varredura a laser) dos discos de resina foram avaliadas. Em seguida, 10 amostras por grupo foram escovadas com os dentifrícios Máxima Proteção Anticáries, Sensodyne Repair & Protect e Colgate Sensitive Pro-Alívio. A escovação foi realizada com uma escova elétrica com cabeça de cerdas macias, com potência e peso padronizados, durante 30 minutos. A cada 30 segundos, 1,0 ml da pasta era injetada entre as cerdas da escova e a amostra. Após o desafio abrasivo, as amostras tiveram sua cor e rugosidade reavaliadas. Os dados foram submetidos ao teste de Kruskal-Wallis (alteração de cor) ou ao teste t (rugosidade da superfície) (α=5%). A escovação não alterou significativamente a cor dos compósitos. Por outro lado, a rugosidade superficial dos compósitos foi significativamente afetada pelo desafio abrasivo, independentemente do dentifrício utilizado. A alteração da rugosidade superficial foi semelhante para todos os compósitos. O desafio abrasivo com a Máxima Proteção Anticáries, o Sensodyne Repair & Protect e o Colgate Sensitive Pro-Alívio não foi capaz de alterar significativamente a cor das resinas. Diferentemente, os desafios abrasivos alteraram significativamente a rugosidade superficial de todos os compósitos avaliados. No entanto, as mudanças na rugosidade foram estatisticamente semelhantes nos compósitos micro-híbridos e nanoparticulado. (AU)

Effect of Acid Beverage on the Microhardness of Primary Tooth Enamel In Vitro.

Purpose: To assess the effects of a soft drink, a soybean-based apple juice and strawberry juice on the superficial and deep microhardness of primary tooth enamel.
Methods: Sixty primary teeth were divided according to the beverages and a control group (artificial saliva). Immersion cycles were carried out under agitation (five minutes three times a day over 60 days). Superficial microhardness measurements were taken after seven, 15, 30, 45, and 60 days. Teeth were cut for deep microhardness evaluation. Analysis of variance and Tukey's test (95 percent confidence interval) were used for data analysis. Teeth were scanned by electron microscopy for quantitative analysis.
Results: The soybean drink led to a significant decrease in the superficial microhardness ( P <0.05) at all tested times. The decrease for the strawberry juice was steeper than for the soybean drink and the soft drink significantly decreased the superficial microhardness at all times. The soybean drink recorded lower surface deep microhardness values while the juice presented similar results to the soybean drink at a depth of up to 200 µm. There was a gradual and statistically significant increase at a depth of up to 300 µm with the soft drink. Scanning electron microscopy evaluation showed that all beverages had gradual demineralization, being evident on the 60th day; the soft drink showed the greatest overall loss of enamel.
Conclusion: All beverages affected the microhardness of primary teeth enamel. The soft drink was the most harmful to enamel among the assessed beverages.